1.6587 – 18CrNiMo7-6 – 16 326 Alloyed case-hardening steel with excellent surface hardness and a tough core, intended for highly stressed components.
Availability
Availability: In stock
Your price:: 3,20 EUR
without TAX
3,94 EUR incl. tax/kg /kg
3,94 EUR incl. tax/kg /kg
Legal guarantee 2 years (EU notice)
Show information
Application:
For the manufacture of highly stressed machine components such as gears, shafts, pins, and clutch parts that require a hard surface and a tough core.
Properties:
| Property | Value / Description |
|---|---|
| Surface hardness after carburizing | Up to 58–62 HRC |
| Heat treatment | Carburizing, quenching, tempering |
| Machinability | Good in annealed condition, reduced after quenching |
| Weldability | Limited – preheating and subsequent annealing recommended |
| Wear resistance | High (after carburizing) |
Mechanical Properties:
| Property | Value |
|---|---|
| Hardness (HB) | 295 – 384 HB (after heat treatment: carburizing + quenching + tempering) |
| Yield strength Rp0.2 (MPa) | 685 – 835 MPa |
| Tensile strength Rm (MPa) | 980 – 1,420 MPa |
| Elongation A₅ (%) | 5 – 10 % |
Chemical Composition:
| Element | Content (%) |
|---|---|
| C | 0.15 – 0.21 |
| Si | ≤ 0.40 |
| Mn | 0.50 – 0.90 |
| P | ≤ 0.025 |
| S | ≤ 0.035 |
| Cr | 1.50 – 1.80 |
| Ni | 1.40 – 1.70 |
| Mo | 0.25 – 0.35 |
Navštívili ste
Round bar rolled diameter 150 mm 1.6587 - 18CrNiMo7-6 - 16 326
Parameters
Shape:Kruhový
Material type:Oceľ
Material:1.6587 - 18CrNiMo7-6 - 16 326
Length (mm):3000
3,20 EUR
without TAX
3,94 EUR incl. tax
3,94 EUR incl. tax
Availability
Availability: In stock
Professional advice
DOBROSTEEL s.r.o. provides comprehensive expert advice in the selection, processing, and use of steels. With many years of experience in the steel industry, we can recommend the right material based on the required mechanical properties, processing method, and intended application.
7:00 AM – 3:00 PM