Round bar peeled diameter 162 mm 1.2344 - X40CrMoV5-1 - 19 554
Round bar peeled diameter 162 mm 1.2344 - X40CrMoV5-1 - 19 554
1.2344 – X40CrMoV5-1 – 19 554 High-alloy tool steel for hot work applications. It is characterized by excellent resistance to thermal fatigue, wear, and good toughness at elevated temperatures.
Availability
Availability: In stock
Your price:: 5,90 EUR
without TAX
7,26 EUR incl. tax/kg /kg
7,26 EUR incl. tax/kg /kg
Legal guarantee 2 years (EU notice)
Show information
Application:
It is primarily used for the production of tools subjected to high thermal and mechanical stress, such as dies, aluminum pressure casting molds, and hot cutting knives.
Properties:
| Property | Description |
|---|---|
| Hardness after quenching | 48–52 HRC |
| Wear resistance | High |
| Resistance to thermal fatigue | Very high |
| Toughness | Good even at elevated temperatures |
| Machinability | Good (in annealed condition) |
| Weldability | Limited (preheating and heat treatment recommended) |
Mechanical Properties:
| Mechanical Property | Value |
|---|---|
| Tensile strength (Rm) | 900 – 1100 MPa |
| Yield strength (Re) | 600 – 850 MPa |
| Elongation (A5) | 10 – 15 % |
| Hardness (HB) | approx. 450 – 520 HB |
Chemical Composition:
| Element | Content (%) |
|---|---|
| Carbon (C) | 0.37 – 0.44 |
| Chromium (Cr) | 4.8 – 5.5 |
| Molybdenum (Mo) | 1.1 – 1.5 |
| Vanadium (V) | 0.9 – 1.3 |
| Manganese (Mn) | 0.2 – 0.5 |
| Silicon (Si) | 0.8 – 1.2 |
| Phosphorus (P) | ≤ 0.025 |
| Sulfur (S) | ≤ 0.015 |
Navštívili ste
Round bar peeled diameter 162 mm 1.2344 - X40CrMoV5-1 - 19 554
Parameters
Shape:Kruhový
Material type:Oceľ
Material:1.2344 - X40CrMoV5-1 - 19 554
Length (mm):3000
5,90 EUR
without TAX
7,26 EUR incl. tax
7,26 EUR incl. tax
Availability
Availability: In stock
Professional advice
DOBROSTEEL s.r.o. provides comprehensive expert advice in the selection, processing, and use of steels. With many years of experience in the steel industry, we can recommend the right material based on the required mechanical properties, processing method, and intended application.
7:00 AM – 3:00 PM